Wear plate application:

1) thermal power plant coal machine cylinder liner grinding speed, fan impeller socket shell, precipitator entrance flue ash duct, bucket lining plate, separator connecting tube, crusher and crusher hopper liner, liner, burner, coal hopper and hopper liner, air pre heater bracket supporting tile the guide vane separator. These parts of the wear-resistant steel plate hardness and abrasion resistance is not too high requirements, you can use the material for NM360/400 thickness of 6-10mm wear-resistant steel plate.

2): coal feeding tank and hopper liner, hopper liner, fan blade, pusher plate, cyclone dust collector, coke guide plate, ball mill lining, auger bit stabilizer, bell and base, kneading machine bucket lining ring feeder, bucket bottom plate. The operation environment of the coal yard is bad, and the corrosion resistance and abrasion resistance of the wear-resistant steel plate are required. It is recommended to use the wear-resistant steel plate with NM400/450 HARDOX400 and 8-26mm thickness.

3) cement factory: chute lining, end bushing, cyclone separator, blades and guide vanes, fan blades and recovery bucket lining, lining, screw conveyor plate, pipe assembly, frit cooling plate lining, conveying groove plate. These components also need wear resistance, corrosion resistance, better wear resistant steel plate, can use material for NM360/400, HARDOX400 thickness of 8-30mmd wear-resistant steel plate.

4) loading unloading machinery: rolling mill chain plate, hopper liner, grab the edge plate, the automatic dump truck dump truck body plate. This requires wear-resistant, high strength and high hardness of wear-resistant steel plate, it is recommended to use the material for NM500 HARDOX450/500 thickness of 25-45MM wear-resistant steel plate.

5) mining machinery: mineral materials, stone, crusher, lining board, blade, conveyor lining plate, baffle. Such components need extremely high wear resistance, available material is NM450/500, HARDOX450/500 thickness of 10-30mm wear-resistant steel plate.

6) construction machinery: Cement pusher, toothed plate, concrete mixer, mixer lining, dust collector, lining board, brick machine, mold board. Wear resistant steel plate of NM360/400 thickness 10-30mm is recommended.

7) construction machinery: loader, bulldozer, excavator bucket board, side blade, bucket bottom plate, blade, rotary drilling rig, drill rod. Such machines require particularly tough and wear-resistant high strength wear-resistant steel plate, available material for NM500, HARDOX500/550/600 thickness of 20-60mm in high strength wear-resistant steel plate.

8) metallurgical machinery: iron ore sintering machine, conveying elbow, iron ore sintering machine lining board, scraper machine lining board. Because of this kind of machine, it needs high temperature resistant and hard wearing steel plate. It is recommended to use HARDOX600HARDOXHiTuf series wear-resistant steel plate.

9) wear-resistant steel plate can also be used in sand mill cylinder, blade, a variety of freight yard, wharf machinery, then parts, bearings, structural parts, railway wheel structure, roller and so on.

Chemical composition: This is the Wugang enterprise standard: WYJ112-2008 chemical composition

Ingredients

Manufactor

C

Si

Mn

P

S

Cr

Mo

Ni

B

Grade

WNM360

Wugang

Less than or equal to 0.25

Less than or equal to 0.70

Less than or equal to 1.30

Less than or equal to 0.025

Less than or equal to 0.010

Less than or equal to 1.4

Less than or equal to 0.50

Less than or equal to 1

Less than or equal to 0.004

Mechanical property:

This is the Wugang enterprise standard: WYJ112-2008 mechanical performance

Grade

Manufactor

hardness

tensile property

20 AKV

Horizontal J

RP0.2

Rm

A50%

MPa

MPa

WNM360

Wugang

320~400

More than 800

More than 1000

More than 10

provide

The steel's physical property, yield strength is about 1000MPa, tensile strength is about 1100MPa.